Admixture for modifying of mortars on cement and gypsum binders. Increases the ductility and fluidity of concrete, cement-sand mixtures and mixtures with low modification. Reduces the tendency to crack formation, increases adhesion.
- The material is ready for use
- The mortar becomes more elastic
- Allows to facilitate the processes of mortars spraying, laying and screeding
- Increases adhesion to mineral bases
- The congealed mortars tendency to cracking and peeling from the base is reduced
GLIMS®Elastic application table in % of cement in mortar
PREPARATION
At material application and solidification the temperature of the lower stratum and the environment must not be lower than +5°C. The material is environmentally friendly in use and operation. Operation temperature range is from -50 to +70 ° С.
TECHNOLOGY OF WORK EXECUTION
Use latex admixture in mortar mix B in the amount of 5-20% of the cement weight at the time of mixing instead of part of the water. The more GLIMS®Elastic is introduced, the more elastic the set material is. Mix the required amount of latex admixture with pure water and use the resulting mortar instead of water for blended cements mixing, following the table for corresponding materials solutions preparation.
RECOMMENDATIONS
When in use the temperature of air, the lower stratum and GLIMS®Elastic should be from +5 to + 35°C. Always observe the above order and proportions for mixing GLIMS® Elastic with other materials. In hot and windy weather take measures to protect against excessive drying of the applied mortars. Do not use GLIMS®Elastic as a primer.
CONSUMPTION
0,05–0,15 l per 1 kg of cement.
PACKAGING
a can of 2, 5, 10 l.
TRANSPORTATION AND STORAGE
Transport under conditions ensuring the integrity of the packaging. Store at a temperature from +5 to + 30 °, protect from frost and direct exposure to sunlight. The storage period in undamaged packing is 12 months. TU5775-007-40397319-2004№Г-7010